SUS410
13Cr Stainless Steel
<Composition> 13Cr
comparison of corrosion resistance
Std.
Applications
Cutlery, machine parts, valves, etc.
Chemical composition
| Type | Standards | Chemical composition (%) | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| JFE Standards | JIS Standards | Correspoding EN Standard | ASTM AISI equivalent |
C | Si | Mn | P | S | Cr | Mo | Other | |
| Std. | SUS410* | 1.4006 | 410 | ≤ 0.15 | ≤ 1.00 | ≤ 1.00 | ≤0.040 | ≤0.030 | 11.50 - 13.50 | |||
Please contact us if you need any special steels not listed above.
Yield strength testing is performed as and when specified.
Hardness is tested as Hv or HRB depending on thickness.
Mechanical properties
| Type | Standards | Mechanical properties | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| JFE Standards | JIS Standards | Correspoding EN Standard | ASTMAISI-equivalent | Tensile test | Hardness test | Bend test | |||||
| Yield strength N/mm² |
Tensile strength N/mm² |
Elongation (%) | Hv | HRB | Bending angle | Inside radius t : thickness |
|||||
| Std. type | SUS410* | 1.4006 | 410 | ≥ 205 | ≥ 440 | ≥ 20 | ≤ 210 | ≤ 93 | 180° | 1.0 × t | |
*Please feel free to consult us about your needs.
Please contact us if you need any special steels not listed above.
Yield strength testing is performed as and when specified.
Hardness is tested as Hv or HRB depending on thickness.
Physical properties
| Steel grade | Density | Electrical Resistance | Magnetism | Specific heat | Thermal conductivity | Thermal expansion coefficient | Young’s modulus | ||
|---|---|---|---|---|---|---|---|---|---|
| 0 - 100℃ | 100℃ | 500℃ | 20 - 100℃ | 20 - 650℃ | ×10³ | ||||
| g/cm³ | 10-6Ω・cm | (Annealed material) | J/kg・℃ （cal /g・℃） |
W /m・℃ （10-2cal /cm・sec・℃） |
10-6/℃ | N/mm² | |||
| SUS410 | 7.75 | 57 | Yes | 460 (0.110) |
24.9 (5.950) |
25.7 (6.860) |
9.9 | 11.7 | 200 |
<<Note>> Density in the table above is the actually measured value as a physical property.
In mass calculations for commercial transactions, JIS G 4310 “Method of Mass Calculation for Stainless Steel Plates and Sheets, and Heat-Resisting Steel Plates and Sheets” will apply.
In mass calculations for commercial transactions, JIS G 4310 “Method of Mass Calculation for Stainless Steel Plates and Sheets, and Heat-Resisting Steel Plates and Sheets” will apply.