Tensile Properties at Romm Temperature
Tensile Properties Specifications
Flow Stress
Susceptibility to Hot Deformation Crackings
Superplastic Formability
Fatigue Strength
Typical Tensile Properties at Elevated Temperature |
| |
 |
| Tensile Properties at Room Temperature |
| |
| (1)Sheet(Mill annealed) |
Thickness
(mm) |
Test Sample Direction |
Tensilel Properties |
Bend Factor
( R / t ) |
UTS
(N/mm2) |
0.2%PS
(N/mm2) |
EI
(%) min |
| 0.5 |
L |
1064 |
1028 |
10 |
- |
| T |
1058 |
1023 |
12 |
| 1.0 |
L |
1038 |
985 |
11 |
2.0 |
| T |
1039 |
996 |
12 |
| 3.0 |
L |
1027 |
965 |
16 |
2.5 |
| T |
1031 |
972 |
15 |
| 5.0 |
L |
1007 |
932 |
15 |
2.5 |
| T |
1034 |
968 |
14 |
|
| |
| (2)Round Bar(ø:25mm) |
| Heat Treatment |
Conditions |
Tensile Properties |
UTS
(N/mm2) |
0.2%PS
(N/mm2) |
El
(%)min |
R.A.
(%) |
| Mill Anneal |
720ºC/1hr/AC |
1020 |
948 |
21 |
42 |
| STA |
830ºC/1hr/AC
+570ºC/3hr/AC |
1130 |
1032 |
16 |
39 |
| STA |
830ºC/1hr/OQ
+540ºC/3hr/AC |
1200 |
1069 |
12 |
25 |
| |
| Ti-6Al-4V-STA |
955ºC/1.5hr/WQ
+570ºC/6hr/AC |
1070 |
998 |
15 |
30 |
|
| STA : Solution treatment + Aging |
| |
| TOP of The Page |
|
| Tensile Properties Specifications |
| |
| AMS 4899 Minimum Tensile Properties(Sheet/Plate) |
| Thickness (mm) |
UTS (N/mm2) |
0.2%PS (N/mm2) |
E I (%) |
| ~ 0.64, excl |
924 |
869 |
6 |
| 0.64 ~ 1.60, excl |
924 |
869 |
8 |
| 1.60 ~ 4.75, excl |
924 |
869 |
10 |
| 4.75 ~ 101.60, excl |
896 |
827 |
10 |
|
| |
| AMS 4964 Minimum Tensile Properties(Bar/Billet) |
| Diameter (mm) |
UTS (N/mm2) |
0.2%PS (N/mm2) |
E I (%) |
R.A (%)
L T |
| ~50.80, incl |
931 |
862 |
10 |
25 |
- |
| 50.80 ~ 101.60, incl |
896 |
827 |
10 |
25 |
20 |
| 101.60 ~ 152.40, incl |
896 |
827 |
10 |
25 |
20 |
|
| |
| TOP of The Page |
|
| Flow Stress |
 |
| |
| TOP of The Page |
|
| Susceptibility to Hot Deformation Cracking |
 |
| |
| TOP of The Page |
|
| Superplastic Formability |
 |
| |
| TOP of The Page |
|
| Fatigue Strength |
 |
| |
| TOP of The Page |
|
| Typical Tensile Properties at Elevated Temperature |
  |
| |