SP-700 alloy possesses a number of excellent properties superior to those of the most widely used alloy, Ti-6Al-4V.Because of this, SP-700 has recieved growing attention from around the world. For high strength and excellent formability, examine the superior properties of SP-700.
Characteristic SP-700 Ti-6Al-4V
Tensile strength 10-15% higher than Ti-6Al-4V, for less weight, reduced thickness and ability to produce larger parts.
Fatigue strength 10-15% higher than Ti-6Al-4V, for increased durability and reliability.
Formability Hot working Cracking sensitivity is low. Permits hot working at lower temperatures, which minimizes costs and makes open-air forging possible.
Superplastic forming Lower superplastic forming temperature and higher elongation than Ti-6Al-4V decreases fabrication costs significantly and makes the fabrication of complicated parts possible.
Cold working Cold rolling, blanking and bending workability are improved greatly. Unlike Ti-6Al-4V, precision blanking is possible.
Heat treatment
response		 Improved hardenability compared to Ti-6Al-4V makes heat treatment of larger parts possible and suppresses distortion during heat treatment.
 
We also offer a derived alloy as a plate material for the golf club face,
having the same outstanding features of the SP-700 but with higher modulus.
Please contact us for further information.
Microstructure
SP-700 Ti-6Al-4V
 
Superplasticity

Superplastic elongation over 2000%